Magasan ötvözött hegesztőhuzalok és AWI pálcák |
Típus |
Szabvány |
Kémiai összetétel (%) |
Hegesztőáram |
S 7403 |
WNr.: |
1.4337 |
AWS A 5.9: |
ER 312 |
EN 12 072: |
G 29 9 / W 29 9 |
|
C:  |
0,120 max. |
Si:  |
0,500 |
Mn:  |
1,700 |
Cr:  |
30,000 |
Ni:  |
9,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7407 |
WNr.: |
1.4370 |
AWS A 5.9: |
ER 307 L |
|
C:  |
0,100 max. |
Si:  |
0,600 |
Mn:  |
6,500 |
Cr:  |
19,000 |
Ni:  |
9,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7407 |
WNr.: |
1.4370 |
AWS A 5.9: |
ER 307 L |
|
C:  |
0,100 max. |
Si:  |
0,600 |
Mn:  |
6,500 |
Cr:  |
19,000 |
Ni:  |
9,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7408 |
WNr.: |
1.4316 |
AWS A 5.9: |
ER 308 L Si |
EN 12 072: |
G 19 9 LSi / W 19 9 LSi |
|
C:  |
0,025 max. |
Si:  |
0,800 |
Mn:  |
1,900 |
Cr:  |
20,000 |
Ni:  |
10,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7408 |
WNr.: |
1.4316 |
AWS A 5.9: |
ER 308 L Si |
EN 12 072: |
G 19 9 LSi / W 19 9 LSi |
|
C:  |
0,025 max. |
Si:  |
0,800 |
Mn:  |
1,900 |
Cr:  |
20,000 |
Ni:  |
10,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7409L |
WNr.: |
1.4332 |
AWS A 5.9: |
ER 308 L Si |
EN 12 072: |
G 23 12 LSi / W 23 12 LSi |
|
C:  |
0,030 max. |
Si:  |
0,500 |
Mn:  |
1,70 |
Cr:  |
24,000 |
Ni:  |
12,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7409L |
WNr.: |
1.4332 |
AWS A 5.9: |
ER 308 L Si |
EN 12 072: |
G 23 12 LSi / W 23 12 LSi |
|
C:  |
0,030 max. |
Si:  |
0,500 |
Mn:  |
1,70 |
Cr:  |
24,000 |
Ni:  |
12,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7409Mo |
WNr.: |
1.4459 |
AWS A 5.9: |
ER 309 MoL |
|
C:  |
0,030 |
Si:  |
0,600 |
Mn:  |
1,600 |
Cr:  |
23,000 |
Mo:  |
2,400 |
Ni:  |
13,000 |
P:  |
max .< 0,0 |
S:  |
max. <0,02 |
|
|
W 7409Mo |
WNr.: |
1.4459 |
AWS A 5.9: |
ER 309 MoL |
|
C:  |
0,030 |
Si:  |
0,600 |
Mn:  |
1,600 |
Cr:  |
23,000 |
Mo:  |
2,400 |
Ni:  |
13,000 |
P:  |
max .< 0,0 |
S:  |
max. <0,02 |
|
|
S 7410 |
WNr.: |
1.4842 |
AWS A 5.9: |
ER 310 |
EN 12 072: |
G 25 20 / W 25 20 |
|
C:  |
0,120 max. |
Si:  |
0,500 |
Mn:  |
1,700 |
Cr:  |
25,000 |
Ni:  |
20,500 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7410 |
WNr.: |
1.4842 |
AWS A 5.9: |
ER 310 |
EN 12 072: |
G 25 20 / W 25 20 |
|
C:  |
0,120 max. |
Si:  |
0,500 |
Mn:  |
1,700 |
Cr:  |
25,000 |
Ni:  |
20,500 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7416 |
WNr.: |
1.4430 |
AWS A 5.9: |
ER 316 L |
EN 12 072: |
G 19 12 3 LSi / W 19 12 3 LSi |
|
C:  |
0,025 max. |
Si:  |
0,800 |
Mn:  |
1,800 |
Cr:  |
18,000 |
Mo:  |
2,500 |
Ni:  |
12,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7416 |
WNr.: |
1.4430 |
AWS A 5.9: |
ER 316 L |
EN 12 072: |
G 19 12 3 LSi / W 19 12 3 LSi |
|
C:  |
0,025 max. |
Si:  |
0,800 |
Mn:  |
1,800 |
Cr:  |
18,000 |
Mo:  |
2,500 |
Ni:  |
12,000 |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7418 |
WNr.: |
1.4576 |
AWS A 5.9: |
ER 318 |
EN 12 072: |
G 19 12 3 NbSi/W 19 12 3 NbSi |
|
C:  |
0,050 max. |
Si:  |
0,700 |
Mn:  |
1,400 |
Cr:  |
18,500 |
Mo:  |
2,600 |
Ni:  |
11,500 |
Nb:  |
12x C min. |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7418 |
WNr.: |
1.4576 |
AWS A 5.9: |
ER 318 |
EN 12 072: |
G 19 12 3 NbSi/W 19 12 3 NbSi |
|
C:  |
0,050 max. |
Si:  |
0,700 |
Mn:  |
1,400 |
Cr:  |
18,500 |
Mo:  |
2,600 |
Ni:  |
11,500 |
Nb:  |
12x C min. |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
S 7447 |
WNr.: |
1.4551 |
AWS A 5.9: |
ER 347 |
EN 12 072: |
G 19 9 NbSi / W 19 9 NbSi |
|
C:  |
0,070 max. |
Si:  |
0,700 |
Mn:  |
1,700 |
Cr:  |
19,500 |
Ni:  |
10,000 |
Nb:  |
12x C min. |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|
W 7447 |
WNr.: |
1.4551 |
AWS A 5.9: |
ER 347 |
EN 12 072: |
G 19 9 NbSi / W 19 9 NbSi |
|
C:  |
0,070 max. |
Si:  |
0,700 |
Mn:  |
1,700 |
Cr:  |
19,500 |
Ni:  |
10,000 |
Nb:  |
12x C min. |
P:  |
0,020 max. |
S:  |
0,015 max. |
|
|